Went to the range today equipped with my new laser thermometer. Found out that the barrel temperature half way down the barrel was 20 degrees hotter then at the chamber. Why then does fire cracking appear at the chamber?
Fire Cracking and Barrel Heat
- Thread starter centershot
- Start date
Yea, the highest temps are at the chamber area at time of ignition. It probably does cool faster than down the barrel a ways due to the opening at the chamber area as cooler air can enter quicker.
Multiracer
Gold $$ Contributor
...and midway down the barrel the friction is greatest.
A follow up question > when a barrel fire cracks it is said to be hard on reamers to re chamber or set back, so without assuming can some one explain just what’s going on that increases the level of difficulty and is the barrel now hardened like heat treating a tool ?
Dumb question I know..
Dumb question I know..
You're tempering the steel. It cracks because it has lost all of it elasticity, hence cracking. Eventually it will be as hard as the reamer.
DaveTooley
Gold $$ Contributor
E
Tempering is used to reduce the hardness of the steel. 416SS will only get to about Rc 40. 28-32 is the range of the steel when a barrel is made. Heat checking is impregnated with carbon from powder residue. Carbon is hard and shortens the life span of the throat area.
@DaveTooley
This barrel only has 1142 rounds, I was thinking about a set back although I’m not sure if it would be a good candidate or if it’s too far gone.
This barrel only has 1142 rounds, I was thinking about a set back although I’m not sure if it would be a good candidate or if it’s too far gone.
Attachments
DaveTooley
Gold $$ Contributor
If you're doing the work then maybe. If you have to pay someone then I wouldn't do it.
jelenko
Gold $$ Contributor
Hmmm. The lands look smooth. The stuff in the grooves - is it carbon?
My lands show cracking before the grooves.
TTE
Gold $$ Contributor
I’m not sure, I may clean it again and take another look.
It still shoots ok, just not competitive as a 1000 yard BR barrel needs to be. Better for local practice or fun match etc.
Jim
Thanks Dave, I appreciate the input.
Jim
6.5 forever
Silver $$ Contributor
DaveTooley
Gold $$ Contributor
Pic #1&2 are the top of the lands. Lands make 100% contact with the bullet and have the highest barrel to bullet pressure. Thus higher temperatures. Thus heat checking.
TTE
Gold $$ Contributor
Yes. Put on some vinyl tubing and stick it in the chamber. Trigger is on/off (don't have to hold it on), moves a lot of air (24 CFM) and with the extended battery lasts 3 hours of run time. I like mine !
Shooter13
Gold $$ Contributor
Heres the deal for me and I'm not a @DaveTooley as I'm sure he had forgotten more than I'll ever know about this stuff, the 3rd picture of the chamber end doesn't look bad to me at all! What is the target telling you? I have barrels that shoot great and look far worse than that!! Sometimes I think maybe they shouldn't have given shooters a barrel scope 
The target is why I pulled the barrel, it just was no longer competitive as tuned. So rather than using up more H4895 and primers, I swapped it out for a new barrel that shoots half the size.
Jim
Upgrades & Donations
This Forum's expenses are primarily paid by member contributions. You can upgrade your Forum membership in seconds. Gold and Silver members get unlimited FREE classifieds for one year. Gold members can upload custom avatars.
Click Upgrade Membership Button ABOVE to get Gold or Silver Status.
You can also donate any amount, large or small, with the button below. Include your Forum Name in the PayPal Notes field.
To DONATE by CHECK, or make a recurring donation, CLICK HERE to learn how.
Click Upgrade Membership Button ABOVE to get Gold or Silver Status.
You can also donate any amount, large or small, with the button below. Include your Forum Name in the PayPal Notes field.
To DONATE by CHECK, or make a recurring donation, CLICK HERE to learn how.