		Since WSSM brass is as rare as hen's teeth (or extremely pricey) do any of you have any opinions about case forming a 270 WSM down to 243 WSSM?  I realize the shoulder would probably end up being thicker and the neck also.  I suppose that would involve neck turning and/or reaming.  Might have to anneal multiple times during the process.
What say you??
				