Which Loctite for gunsmithing uses?

[Oldeadeye]

Jepp2 mentioned in his post above about using Vibra Tite VC3. It is a mil-spec thread locker. It’s also reusable. You apply it to the threads and let it “cure”. It only takes a few minutes. It cures to a rubber like consistency. You can install and remove the fastener several times before having to apply new material. What I like is that it doesn’t effect torque value.

 

[Luisyamaha]

I've used the red Loc-tite under the scope bases, without getting any on the screws, without any ill effects. Kinda like bedding the bases. Definitely would not move. Come off easily enough with a little heat or a solid whack from a hammer. The Loc-tite residue came off, I think, with acetone. Or heat. Or both. In any case it was not that big a deal.

Luisyamaha

 

[Drop Port]

Clear finger nail polish works good. Pick your color.

For picking up guys?

 

[Outrider27]

Jepp2 mentioned in his post above about using Vibra Tite VC3. It is a mil-spec thread locker. It’s also reusable. You apply it to the threads and let it “cure”. It only takes a few minutes. It cures to a rubber like consistency. You can install and remove the fastener several times before having to apply new material. What I like is that it doesn’t effect torque value.

Forgot to mention jepp2's question about VC3 in my last post. I've used it too, with the same experiences you have had. For scope bases and scope rings and the like, it might well be the best choice - clean, easy to apply, and doesn't migrate when applied and cured according to directions. Plus you can apply it to a screw and store the screw pretty much indefinitely and it will be ready to go next time you want to use a screw in a thread locker situation.

 

[snakepit]

Video by Brownells.

About Loctite, I'm not saying yes or no, just saying.

https://www.brownells.com/guntech/quick-tip-how-to-properly-use-loctite-/detail.htm?lid=17367

 

[Iowa Fox]

Loctite and its many different grades is a wonderful product. All you have to do is buy a used action with a base attached with the wrong grade and you will be cussing in a hurry, heat or no heat.

 

[M-61]

Any lube on the threads will increase the preload on the screw, sometimes dramatically.

It sure does. There are charts giving the torque reduction needed when using specific lubricants. Some are as high as 60% reduction. (depends also on bolt size)